Deformation and annealing study of Nicraly

Extensive experiments were carried out on the ODS alloy Nicraly, (an alloy prepared by mechanical alloying and consolidating a powder blend consisting of 16% chromium, 4% aluminum, 2-3% yttria, balance nickel), in efforts to develop methods of controlling the grain size and grain shape of the material. The experiments fell into two general categories: variations in the annealing parameters using the as-extruded material as it was received, and various thermomechanical processing schedules (various combinations of cold work and annealing). Success was achieved in gaining grain size and grain shape control by annealing of the as-extruded material. By proper selection of annealing temperature and cooling rates, the grain size of the as-received material was increased almost two orders of magnitude (from an average grain dimension of 0.023 mm to 1.668 mm) while the aspect ratio was increased by some 50% (from 20:1 to 30:1). No success was achieved in gaining significant control of the grain size and shape of the material by thermo-mechanical processing