Automated fabrication of back surface field silicon solar cells with screen printed wraparound contacts

The development of a process for fabricating 2 x 4 cm back surface field silicon solar cells having screen printed wraparound contacts is described. This process was specifically designed to be amenable for incorporation into the automated nonvacuum production line. Techniques were developed to permit the use of screen printing for producing improved back surface field structures, wraparound dielectric layers, and wraparound contacts. The optimized process sequence was then used to produce 1852 finished cells. Tests indicated an average conversion efficiency of 11% at AMO and 28 C, with an average degradation of maximum power output of 1.5% after boiling water immersion or thermal shock cycling. Contact adherence was satisfactory after these tests, as well as long term storage at high temperature and high humidity