Add to ORKGThe various steps involved in the chemical polishing and etching of silicon samples are described and the data on twins, grain boundaries and dislocation pits from fifty-three (53) samples are discussed
Research on the structural defects of silicon such as grain boundaries and dislocations, their spati...
Bar specimens were cut from ingots of single crystal silicon, and acid etched prior to testing. Arti...
Liquid diffusion masks and liquid applied dopants to replace the CVD Silox masking and gaseous diffu...
The various steps involved in the chemical polishing and etching of silicon samples are described. D...
The various steps involved in obtaining quantitative information of structural defects in crystallin...
One hundred ninety-three silicon sheet samples, approximately 880 square centimeters, were analyzed ...
Statistically significant quantitative structural imperfection measurements were made on samples fro...
The technical and economic feasibility of producing solar-cell-quality sheet silicon was investigate...
The technical feasibility of producing solar cell quality sheet silicon to meet the DOE 1986 cost go...
A program is described which supports and promotes the development of processing techniques which ma...
The limits of blade tolerance were defined. The standard blades are T-2 thickness tolerance. Good re...
The objective of this research program is to investigate the technical and economic feasibility of p...
Significant progress is reported in fabricating a 4 sq cm cell having a 10.1 percent conversion effi...
Testing of low cost low suspension power slurry vehicles is presented. Cutting oils are unlikely to ...
The effects of impurities, various thermochemical processes, and any impurity-process interactions u...
Research on the structural defects of silicon such as grain boundaries and dislocations, their spati...
Bar specimens were cut from ingots of single crystal silicon, and acid etched prior to testing. Arti...
Liquid diffusion masks and liquid applied dopants to replace the CVD Silox masking and gaseous diffu...
The various steps involved in the chemical polishing and etching of silicon samples are described. D...
The various steps involved in obtaining quantitative information of structural defects in crystallin...
One hundred ninety-three silicon sheet samples, approximately 880 square centimeters, were analyzed ...
Statistically significant quantitative structural imperfection measurements were made on samples fro...
The technical and economic feasibility of producing solar-cell-quality sheet silicon was investigate...
The technical feasibility of producing solar cell quality sheet silicon to meet the DOE 1986 cost go...
A program is described which supports and promotes the development of processing techniques which ma...
The limits of blade tolerance were defined. The standard blades are T-2 thickness tolerance. Good re...
The objective of this research program is to investigate the technical and economic feasibility of p...
Significant progress is reported in fabricating a 4 sq cm cell having a 10.1 percent conversion effi...
Testing of low cost low suspension power slurry vehicles is presented. Cutting oils are unlikely to ...
The effects of impurities, various thermochemical processes, and any impurity-process interactions u...
Research on the structural defects of silicon such as grain boundaries and dislocations, their spati...
Bar specimens were cut from ingots of single crystal silicon, and acid etched prior to testing. Arti...
Liquid diffusion masks and liquid applied dopants to replace the CVD Silox masking and gaseous diffu...