A study on the electrolysis of sulfur dioxide and water for the sulfur cycle hydrogen production process

Experimental electrolysis cells using various platinum catalyzed carbon electrodes were tested. When operated at 200 mA/sq cm current density using 50 w/o acid at 50 C and 1 atm, a reference cell required 1.22 volts and degraded rapidly. After several improvements were incorporated into electrodes and the test cell configuration, a later cell required only 0.77 volts under identical operating conditions. At a lower current density, 100 mA/sq cm, the cell required only 0.63 volts. Kinetic studies on metal electrodes, measurements of temperature effects on electrode kinetics, investigations of electrocatalytic activities of metal electrodes over a wide range of acid concentrations, cyclic voltametric studies and evaluation of alternate catalysts were also conducted. From diffusivity experiments, a cation exchange membrane material, P-4010, exhibited an excellent diffusion coefficient, more than two orders of magnitude lower than that of rubber. Ionic resistivity measurements of eight materials showed that microporous rubber had the lowest resistivity