Surface temperatures and glassy state investigations in tribology, part 4

Measurements were made of the limiting shear stress for two naphthenic oils of differing molecular weight and three blends of the lower molecular weight oil and polyalkylmethacrylate polymers of differing molecular weight. The two base oils reached the same limiting shear stress for the same temperature and pressure. This was also true for all the polymer solutions although the polymer reduced the limiting shear stress by about 15 percent. It is shown that limiting stress is more a function of material type than viscosity or molecular weight. A new falling body viscometer was constructed to operate to 230 C and 0.6 GPa. Another viscometer was constructed to extend the pressure range to 1.1 GPa. A concentrated contact simulator was developed which allows recording of the traction force while the slide-roll ratio is continuously varied and the rolling speed is maintained essentially constant by a single drive motor. The configuration is that of a crowned roller against a disk. Measurement of lubricant minimum film thickness of elliptical EHD contacts of various aspect ratios were made by optical interferometry. The data collected were used to evaluate the Hamrock and Dowson minimum film thickness model over a range of contract ellipticity ratio where the major axis of the contact ellipse was aligned both parallel and perpendicular to the direction of motion. A statistical analysis of the measured film thickness data showed that on the average the experimental data were 30 percent greater than the film thickness predicted by the model. Preliminary development of the application of a scanning infrared radiation system to a tribo-system was completed