The influence of elevated and cryogenic temperatures on the elastic moduli and fracture strengths of several C6000/PMR-15 and C6000/NR-15082 laminates was measured. Tests were conducted at -157 C, 24 C, and 316 C (-250 F, 75 F, and 600 F). Both notched and unnotched laminates were tested. The average stress failure criterion was used to predict the fracture strength of quasi-isotropic notched laminates
Analyses of Graphite/Polyimide laminates shown that the thermomechanical strains cannot be separated...
State-of-the-art, high temperature polyimide matrix composites, reinforced with continuous graphite ...
Two graphite/polyimide composite materials were aged in circulating air ovens at temperatures 204 C,...
Thermal and air environment effects on mechanical properties of graphite/polyimide laminate
Experimental results are presented for the elastic and strength properties of T300/5208 graphite-epo...
Seventy-nine graphite/polyimide compression specimens were tested to investigate experimentally the ...
Edge delamination tension and double cantilever beam tests were used to characterize the interlamina...
A design allowables test program was conducted on Celion 6000/LARC-160 graphite polyimide composite ...
Tensile tests were conducted on 0 unidirectionally reinforced Celion 6000 graphite fibers in PMR-15 ...
A study was conducted to assess the merits of using graphite/polyimide, NR-150B2 resin, for structur...
Results are presented from an experimental evaluation of IM7/977-2, IM7/F655, and T800/F3900. Data p...
Sixteen ply, quasi-isotropic laminates of Celanese Celion 6000/PMR-15 and Celion 6000/LARC-160 with ...
To support the development of new materials for the design of next generation supersonic transports,...
A design allowables test program was conducted on Celion 3000/PRM-15 and Celion 6000/PMR-15 graphite...
Experimental data for the thermal conductivity, thermal expansion, specific heat, and emittance of l...
Analyses of Graphite/Polyimide laminates shown that the thermomechanical strains cannot be separated...
State-of-the-art, high temperature polyimide matrix composites, reinforced with continuous graphite ...
Two graphite/polyimide composite materials were aged in circulating air ovens at temperatures 204 C,...
Thermal and air environment effects on mechanical properties of graphite/polyimide laminate
Experimental results are presented for the elastic and strength properties of T300/5208 graphite-epo...
Seventy-nine graphite/polyimide compression specimens were tested to investigate experimentally the ...
Edge delamination tension and double cantilever beam tests were used to characterize the interlamina...
A design allowables test program was conducted on Celion 6000/LARC-160 graphite polyimide composite ...
Tensile tests were conducted on 0 unidirectionally reinforced Celion 6000 graphite fibers in PMR-15 ...
A study was conducted to assess the merits of using graphite/polyimide, NR-150B2 resin, for structur...
Results are presented from an experimental evaluation of IM7/977-2, IM7/F655, and T800/F3900. Data p...
Sixteen ply, quasi-isotropic laminates of Celanese Celion 6000/PMR-15 and Celion 6000/LARC-160 with ...
To support the development of new materials for the design of next generation supersonic transports,...
A design allowables test program was conducted on Celion 3000/PRM-15 and Celion 6000/PMR-15 graphite...
Experimental data for the thermal conductivity, thermal expansion, specific heat, and emittance of l...
Analyses of Graphite/Polyimide laminates shown that the thermomechanical strains cannot be separated...
State-of-the-art, high temperature polyimide matrix composites, reinforced with continuous graphite ...
Two graphite/polyimide composite materials were aged in circulating air ovens at temperatures 204 C,...