Investigation of nickel-silicon metallization process

The metallization of silicon solar cells passivated with silicon nitride coating was investigated by using commercial Ni pastes #5517 from Thick Film Systems, #7028-5 from Cermalloy, experimental formulation # X-A by Sollos, Inc. and evaporated Ti-Ni film. Comparative and reference tests were done with the Dupont Ag paste #7095 and with a mixture of Ni paste #5517 with Ag paste #7095 in the respective ratio of 9 to 1 by weight. The evaluation criteria for the metallization was the mechanical bond strength of the contact, solderability, copper plating ability and electrical characteristics in terms of Voc, Isc values and shape of the V-I curve. The results revealed that the Dupont Ag paste #7095 mt all required criteria, while the quality of the cells metalized with the commercial Ni paste #5517 from Thick Film Systems, #7028-5 from Cermalloy as well as the experimental paste # X-A from Sollos, Inc. was below the acceptable standards. A significant improvement was obtained with the mixture of Ni paste #5517 from Thick Film Systems with 10% addition of Dupont paste # 7095