Analysis of local delaminations and their influence on composite laminate behavior

An equation was derived for the strain energy release rate, G, associated with local delamination growth from a matrix ply crack. The critical GC for edge delamination onset in 25/902s graphite epoxy laminates was measured and used in this equation to predict local delamination onset strains in 25/90ns, n = 4, 6, 8 laminates. A simple technique for predicting strain concentrations in the primary load bearing plies near local delaminations was developed. These strain concentrations were responsible for reduced laminate nominal failure strains in laminates containing local delaminations. The influence of edge delamination and matrix crack tip delamination on laminate stiffness and strength was compared