Raman spectroscopic investigations of Hg-Cd-Te melts

Raman scattering measurements are reported for a series of Hg sub1-xCd subxTe (with x less than or =0.2) materials from 295 K (room temperature) to 1126K (up to and above their liquidus temperatures), and for Hg sub1-xCd subxTe (x=0.3) at 285K. The samples were contained in high-temperature optically-flat fused silica cell. Variable temperature measurements were effected in a three-zone, high-temperature furnace equipped with optical windows, and monitored externally by three independently programmable temperature controllers. All studies were made in the backscattering geometry using the 5145 A line of an Ar+ ion laser, with incident power less than 250 mW, as the excitiation source. An intensity enhancement is observed for a mode in each of the compositions studied. The frequency of this mode varies with composition, 142/cm for HgTe, and 128/cm for both the Hg sub1-xCd subxTe (x=0.053 and 0.204) samples. In addition, a shift to lower frequency as a function of temperature is observed in all samples. This shift is most prominent for the x=0.053 sample. The temperature dependence of these modes as the liquidus temperatures are achieved and surpassed for these samples is presented as being associated with a structural transition in the Hg-rich compositions of the Hg sub1-xCd subxTe series. To our knowledge, this is the first reported study of Raman scattering by phonons in the melts of these materials