Orbiter Cold Plate Intergranular Corrosion: Development of NDE Standards and Assessment of NDE Methods

During pre-servicing of a space shuttle (orbiter vehicle, OV-102), helium leak detection of an avionics cold plate identified a leak located in the face sheet oriented towards the support shelf. Subsequent destructive examination of the leaking cold plate revealed that intergranular corrosion had penetrated the 0.017-inch thick aluminum (AA6061) face sheet. The intergranular attack (IGA) was likely caused by an aggressive crevice environment created by condensation of water vapor between the cold plate and support shelf. Face sheet susceptibility to IGA is a result of the brazing process used in the fabrication of the cold plates. Cold plate components were brazed at 1000 F followed by a slow cooling process to avoid distortion of the bonded cold plate. The slow cool process caused excessive grain boundary precipitation resulting in a material that is susceptible to IGA. The objectives of this work are as follows: (1) Develop first-of-a-kind nondestructive evaluation (NDE) standards that contain IGA identical to that found in the orbiter cold plates; and (2) Assess advanced NDE techniques for corrosion detection and recommend methods for cold plate examination. This report documents the results of work performed at Langley Research Center to fulfill these objectives