Kinetics of Nucleation and Crystal Growth in Glass Forming Melts in Microgravity

This flight definition project has the specific objective of investigating the kinetics of nucleation and crystal growth in high temperature inorganic oxide, glass forming melts in microgravity. It is related to one1 of our previous NASA projects that was concerned with glass formation for high temperature containerless melts in microgravity. The previous work culminated in two experiments which were conducted aboard the space shuttle in 1983 and 1985 and which consisted of melting (at 1500 C) and cooling levitated 6 to 8 mm diameter spherical samples in a Single Axis Acoustic Levitator (SAAL) furnace. Compared to other types of materials, there have been relatively few experiments, 6 to 8, conducted on inorganic glasses in space. These experiments have been concerned with mass transport (alkali diffusion), containerless melting, critical cooling rate for glass formation, chemical homogeneity, fiber pulling, and crystallization of glass forming melts. One of the most important and consistent findings in all of these experiments has been that the glasses prepared in microgravity are more resistant to crystallization (better glass former) and more chemically homogeneous than equivalent glasses made on earth (1g). The chemical composition of the melt appears relatively unimportant since the same general results have been reported for oxide, fluoride and chalcogenide melts. These results for space-processed glasses have important implications, since glasses with a higher resistance to crystallization or higher chemical homogeneity than those attainable on earth can significantly advance applications in areas such as fiber optics communications, high power laser glasses, and other photonic devices where glasses are the key functional materials. The classical theories for nucleation and crystal growth for a glass or melt do not contain any parameter that is directly dependent upon the g-value, so it is not readily apparent why glasses prepared in microgravity should be more resistant to crystallization than equivalent glasses prepared on earth. Similarly, the gravity-driven convection in a fluid melt is believed to be the primary force field that is responsible for melt homogenization on earth. Thus, it is not obvious why a glass prepared in space, where gravity-driven convection is ideally absent, would be more chemically homogeneous than a glass identically prepared on earth. The primary objective of the present research is to obtain experimental data for the nucleation rate and crystal growth rate for a well characterized silicate melt (lithium disilicate) processed entirely in space (low gravity) and compare these rates with the nucleation and crystal growth rates for a similar glass prepared identically on earth (1g)