Hnědé pigmenty s perovskitovou strukturou SrSnO3: Role mineralizačních přísad

Ceramic pigments of the type SrSn0.8Mn0.2O3 were prepared by classical method. Solid – state reaction of initial components was supported by molten salts that had played role of mineralizers. The selected mineralizers (Li2CO3, NaF: NaCl (1:1), KCl, KCl:K2CO3 (1:1) and Na3AlF6) in a amount of 5 % (w/w) were used. Effect of the type of mineralizer and the calcining temperature on the colour properties, particle size distribution, morphological properties and phase composition was studied. The single – phase product was obtained at calcining temperature of 1200 °C and above. A particle size of d50 was varied in the range 1.1 – 6.5 µm. The pigments prepared were applied into the organic matrix. With a higher calcining temperature, the brown colour of application became darker. The most interesting brown colour of pigment was eventually obtained by calcination of the reaction mixture containing the NaF:NaCl mixture.Keramické pigment typu SrSn0.8Mn0.2O3 byly připraveny klasickou metodou. Reakce výchozích složek v tuhé fázi byla podpořena roztavenými solemi, které měly roli mineralizátorů. Vybrané minelizátory (Li2CO3, NaF: NaCl (1:1), KCl, KCl : K2CO3 (1:1) and Na3AlF6) byly použity v množství 5 hm. %. Byl studován vliv typu mineralizátoru a teploty výpalu na barevné vlastnosti, distribuci velikosti částic, morfologické vlastnosti a fázové složení. Jednofázový produkt byl získán při kalcinační teplotě 1200 °C a vyšší. Střední velikost částic d50 se pohybovala v rozsahu 1,1 – 6,5 µm. Připravené pigment byly aplikovány do organického pojiva. S vyšší teplotou kalcinace docházelo k tmavnutí pigmentu. Nejzajímavější hnědá barva pigmentu byla nakonec získána kalcinací reakční směsi s obsahem mineralizační směsi NaF:NaCl