Vliv podmínek oxidační polymerace anilinu a typu dopantu na morfologii částic PANI

The oxidative polymerization of aniline was studied in order to determine a favourable combination of reaction conditions leading to polyaniline (PANI) nano-sized particles of high aspect ratio and narrow polydispersity. The dimensions and morphology of PANI particles were tuned by the following reaction conditions: oxidant type, reaction temperature, reaction time, way of stirring the reaction mixture, and dopant type. The desired rod-shaped PANI morphology was achieved in the case of aniline oxidative polymerization carried out at 50 °C for 24 h and at constant stirring with a magnetic unit, when using (NH4)2S2O8 as the oxidant. The best aspect ratio under the above-mentioned conditions was reached by using HCl, p-toluenesulphonic acid, and H2SO4; all being used as dopants.Byla studována oxidační polymerace anilinu s cílem určit vhodnou kombinaci reakčních podmínek, které vedou k polyanilinovým(PANI) nanočásticím s vysokým poměrem podélnosti a malou polydisperzitou. Rozměry a morfologie částic PANI byly řízeny pomocí následujících reakčních podmínek: typ oxidantu, reakční teplota, reakční doba, způsob míchání reakční směsi a typ dopantu. Požadované tyčinkovité PANI morfologie bylo dosaženo v případě oxidační polymerace anilinu prováděné při 50 °C po dobu 24 hodin a za stálého míchání s magnetickou jednotkou, při použití (NH4)2S2O8 jako oxidačního činidla. Nejlepšího poměru podélnosti za výše uvedených podmínek bylo dosaženo použitím HCI, kyseliny p-toluensulfonové a H2SO4 jako dopantů