A comparison investigation of optical, structural and luminescence properties of CdOxTe1−x and CdTexSe1−x nanoparticles prepared by a simple one pot method

We present L-cysteine capped CdOXTe1−X and CdTeXSe1−X nanoparticles (NPs) prepared in one pot. The as-prepared CdOXTe1−X NPs were found to have a hexagonal crystal structure of CdTe with a cubic phase of CdO. There was, however, change in phase to cubic type when 2 mM of Se was introduced into the CdTe at 60 min of reaction time. The average crystallite sizes obtained from X-ray diffraction analysis for CdOXTe1−X and CdTeXSe1−X NPs were in the range of 10–36 nm. The diffraction peaks shifted to higher diffraction angle with longer growth time. Scanning electron microscope images display change in shape and size as reaction progress. Photoluminescence (PL) emission was observed to shift from 510–566 nm and 620–653 nm for CdOXTe1−X and CdTeXSe1−X NPs respectively followed by variation in the peak intensities. The emission spectra displayed a good symmetry and a narrow full width at half maximum ranging from 41 to 100 nm in both cases. The absorbance analysis of the as-prepared NPs displayed well-resolved absorption bands. The optical band gaps of the as-prepared NPs were found to decrease with increase in reaction time. Reaction parameters such as pH, reaction time, reaction temperature and the molar concentration could have major effects on the optical properties of the as-prepared nanoparticles hence their need to control them