Acceleration of diffusion processes in the metal - hydrogen system and itts application in thermal treatment of structural materials

The hydrogasodynamics and technology a of melt treatment out of furnace by high-implused jets of neutral gas were studied. The conception of a jet synthesis, blowing regimes and devices to solve problems of melt treatment in ladle was developed. The appropriatenesses of melt degassing and homogenizig in ladle at the blowing by trans- and ultrasonic jets of neutral gas were obtained experimentaly. The approptiatenesses of gas-powder jets outflow were studied and a new class of blowing regimes and devices for powder material injection was developed. The principles of construction and optimization of regime parameters of blowing devices, regimes and devices for melt degassing by trans- and ultrasonic jets of neutral gas to inject the powder materials in a melt, technological decisions, concerning the correction of the chemical composition and temperature of a melt in ladle were developed. The principles of a temperature melting regime optimization were developed. The results obtained were applied in the West-Siberian Metallurgical works. The increase of the metal quality allowed to decrease the reject by 20-30%. The yield of steel was increased by 0,1-0,3%, the steel temperature on tap was decreased by 10-25% the specific expense of cast iron was decreased by 2-4 kg/t, the ferroalloy expense was reduced by 3-8%. The results may be use in steelmakingAvailable from VNTIC / VNTIC - Scientific & Technical Information Centre of RussiaSIGLERURussian Federatio