Betriebliche Selbstvorspannung von Fernwaermeleitungen in der Unterverteilung. Bd. 2 Radiale Zeitstand-Druckfestigkeit von PUR-Schaum in Kunststoffmantelrohren

In this research project, the radial creep pressure behaviour of plastic sheath pipes was determined in systematic series of experiments. The experiments were carried out at temperatures of 140, 150 and 160 C, and at pressure stresses of 0.05, 0.1 and 0.4 N/mm"2. Taking into account a suitable safety factor, one can derive a permissible radial pressure strength of 0.15 N/mm"2 from the results of measurements for the then usual FCKW operated plastic sheath pipes. The CO_2 operated plastic sheath pipes (state of development 1989) proved unsuitable for use at high maximum temperatures. Two 'soft foams' (M90 and R142B) were also tested at 150 C, which are no longer on the market now. (orig./GL)In diesem Forschungsvorhaben wurde erstmals das radiale Zeitstand-Druckverhalten von Kunststoffmantelrohren in systematischen Versuchsreihen ermittelt. Die Versuche wurden bei Temperaturen von 140, 150 und 160 C sowie bei Druckspannungen von 0,05, 0,1 und 0,4 N/mm"2 durchgefuehrt. Aus den Messergebnissen laesst sich fuer die damals ueblichen FCKW-getriebenen Kunststoffmantelrohre (KMR) unter Beruecksichtigung eines angemessenen Sicherheitsbeiwertes eine zulaessige radiale Druckfestigkeit von 0,15 N/mm"2 ableiten. Die CO_2-getriebenen Kunststoffmantelrohre (KMR) (Entwicklungsstand 1989) erwiesen sich fuer den Einsatz bei hohen Maximaltemperaturen als ungeeignet. Daneben wurden bei 150 C punktuell auch zwei 'Soft-Schaeume' (M90 und R142B) geprueft, die heute aber nicht mehr auf dem Markt sind. (orig./GL)SIGLEAvailable from TIB Hannover: F96B340+a / FIZ - Fachinformationszzentrum Karlsruhe / TIB - Technische InformationsbibliothekBundesministerium fuer Bildung, Wissenschaft, Forschung und Technologie, Bonn (Germany)DEGerman