ETUDE DU SEUIL DE FISSURATION A HAUTE FREQUENCE EN FATIGUE ET EN FRETTING-FATIGUE

CE TRAVAIL A ETE CONCENTRE A L'ETUDE DU COMPORTEMENT ET A LA COMPREHENSION DU MECANISME DE FISSURATION A HAUTE FREQUENCE EN FATIGUE ET EN FRETTING-FATIGUE. LES PRINCIPAUX TRAVAUX DANS CETTE ETUDE SONT : DEVELOPPEMENT DE NOUVEAUX SYSTEMES D'ESSAI POUR LA FISSURATION ET LE FRETTING FATIGUE A HAUTE FREQUENCE ; CALCUL NUMERAL DU FACTEUR D'INTENSITE DE CONTRAINTE PAR LES ELEMENTS FINIS (PROGRAMME ANSYS) ; ETUDES EXPERIMENTAUX DU SEUIL DE FISSURATION A HAUTE FREQUENCE EN FATIGUE SUR DE NOMBREUX MATERIAUX (FONTE, ACIERS INOXYDABLES, TOLE MINCE ET ACIERS A RESSORT) ET EN FRETTING-FATIGUE SUR LES ACIERS A HAUTES RESISTANCES ; ANALYSES MICROSTRUCTURELLES DES MECANISMES DE FATIGUE A PARTIR DU MICROSCOPE ELECTRONIQUE A BALAYAGE. LA FATIGUE VIBRATOIRE A HAUTE FREQUENCE EST UN MOYEN PRATIQUE ET FIABLE POUR L'ETUDE DE COMPORTEMENT DE FISSURATION EN FATIGUE. LA FREQUENCE N'A PAS D'EFFET SIGNIFICATIF SUR LE SEUIL DE PROPAGATION. L'AUGMENTATION DE TEMPERATURE DUE A L'ABSORPTION D'ENERGIE ULTRASONIQUE N'EST PAS TRES IMPORTANTE POUR LES ESSAIS DE FISSURATION A FAIBLE VITESSE. COMME EN FATIGUE CONVENTIONNELLE, L'EFFET DU RAPPORT DE CHARGEMENT R ET DE LA FERMETURE DE FISSURE EXISTE EN FATIGUE VIBRATOIRE. LES MECANISMES DE FISSURATION SONT LES MEMES EN FATIGUE VIBRATOIRE QU'EN FATIGUE CONVENTIONNELLE LORSQUE LA COMPARAISON EST POSSIBLE. UN COEFFICIENT DE REDUCTION DE LA LIMITE DE FATIGUE EST TROUVE DE 3,5 FOIS DU AU FRETTING. EN FRETTING-FATIGUE A HAUTE FREQUENCE, LE MECANISME D'AMORCAGE ET PROPAGATION DES FISSURES A ETE ANALYSE, ET LE SITE D'AMORCAGE ET LA DIRECTIONS DE PROPAGATION ONT ETE DEFINIS. LA DUREE DE VIE DU FRETTING-FATIGUE ET DETERMINEE PAR LA PROPAGATION DE LA FISSURE PRINCIPALE. LA MECANIQUE DE LA RUPTURE A ETE UTILISEE POUR PREDIRE LA DUREE DE VIE ET LE SEUIL DE PROPAGATION DE LA FISSURE PRINCIPALE EST CORRESPONDANT A LA LIMITE D'ENDURANCE.PARIS-CNAM (751032301) / SudocSudocFranceF