SYNTHESE PAR EPITAXIE PAR JETS MOLECULAIRES DE FILMS MINCES DE CUPRATES A ECHELLES (SR,CA)CU 2O 3 + 4 (ETUDES STRUCTURALES ET PHYSIQUES)

CE TRAVAIL A PORTE SUR LA SYNTHESE PAR EPITAXIE PAR JETS MOLECULAIRES DE FILMS MINCES D'UNE NOUVELLE FAMILLE DE COMPOSES (SR,CA)CU 2O 3 + 4, SUR LEUR CARACTERISATION STRUCTURALE ET PHYSIQUE. L'OPTIMISATION DES PARAMETRES DE DEPOT A ETE OBTENUE POUR LES SUBSTRATS MGO ET SRTIO 3. NOUS AVONS REUSSI A ELABORE DES ECHANTILLONS BIEN CRISTALLISES SUR TOUTE LA GAMME DE COMPOSITION. (SR 1 - XCA X)CU 2O 3 + 4 AVEC 0X1. UNE ETUDE DETAILLEE PAR DIFFRACTION DE RAYONS X, NOUS A PERMIS DE CARACTERISER LA MAILLE CRISTALLINE DE CETTE STRUCTURE ET DE METTRE EN EVIDENCE LA PRESENCE D'EXTINCTIONS SYSTEMATIQUES DANS LE RESEAU. L'ETUDE PAR MICROSCOPIE ELECTRONIQUE A HAUTE RESOLUTION A CLAIREMENT MIS EN EVIDENCE LA PRESENCE DE PLANS A ECHELLES DE CUIVRE A DEUX MONTANTS CU 2O 3. DU POINT DE VUE DES PROPRIETES PHYSIQUES, ON OBSERVE UN COMPORTEMENT TRES DIFFERENT ENTRE SRCU 2O 3 + 4 ET CACU 2O 3 + 4. LES COMPOSES AU CALCIUM PRESENTENT UNE RESISTIVITE A TEMPERATURE AMBIANTE FAIBLE, DE L'ORDRE DU M.CM, ET POUR CERTAINS UNE TRANSITION METAL-ISOLANT AUX ALENTOURS DE 150 K. NOUS AVONS REALISE DES MESURES D'ABSORPTION X AU SEUIL L 3 DU CUIVRE AFIN D'ESTIMER LA CONCENTRATION ET LA SYMETRIE DES TROUS DE DOPAGE. LA DENSITE DE TROUS DE DOPAGE SELON LES FILMS EST VARIABLE MAIS JAMAIS NULLE. ON OBSERVE EGALEMENT UNE AUGMENTATION DE LA CONDUCTIVITE AVEC LE TRANSFERT DE CHARGE. LA POSSIBILITE DE DOPER LES ECHELLES EN AUGMENTANT LE TAUX D'OXYGENE EN FIN DE DEPOT SEMBLE ETRE VERIFIEE.PARIS-BIUSJ-Thèses (751052125) / SudocCentre Technique Livre Ens. Sup. (774682301) / SudocPARIS12-THIAIS CNRS ICMPE (940732301) / SudocPARIS-BIUSJ-Physique recherche (751052113) / SudocSudocFranceF