Crystallization behavior of poly(lactide)/poly(β-hydroxybutyrate)/talc composites.

The authors thank Dr. Patrice Lefrançois (CNAM) for SEM observations. They are also grateful to Pr. Jack R. Plimmer USDA, Agricultural Research Service, USA for his discussions during this work.International audienceThe morphology and miscibility of commercial poly(lactide) (PLA)/poly(b-hydroxybutyrate) (PHB, from 5 to 20 wt %) blends prepared by melt extrusion method, were investigated using differential scanning calorimetry (DSC) and Fourier transform infra-red spectroscopy (FTIR) observations. The results show that for all the studied blend contents, PLA/PHB blends are immiscible. The effects of PHB and talc on the nonisothermal cold crystallization kinetics of PLA were examined using a differential scanning calorimetry (DSC) at different heating rates. PHB acted as a nucleating agent on PLA and the addition of talc to the blend yielded further improve-ment, since significant increase in the enthalpy peak was observed for samples containing 10 wt % PHB and talc (from 0.5 to 5 phr). The crystallization kinetics were then examined using the Avrami-Jeziorny and Liu-Mo approach. The simultaneous presence of PHB and talc induced a decrease of the crystallization half time. The evolution of activation energies determined with Kissinger's equation suggests that blending with PHB and incorporating talc promote nonisothermal cold crystallization of PLA. The synergistic nucleating effect of PHB and talc was also observed on isothermal crystallization of PLA from the melt