Electrochemical growth of two-dimensional tin nano-platelet as high-performance anode material in lithium-ion batteries

A template free, single-step process is developed for fabrication two-dimensional tin nano-platelets by electrochemical deposition in the presence of Triton X100 (TX100). Electrochemical studies combined with structural characterization revealed that during electrodeposition, TX100 molecules adsorb preferentially on {022} planes of Sn and highly anisotropic growth promotes in [200] direction which results in the formation of platelet morphology. The deposited platelets exhibit a high aspect ratio of 30 (width to thickness) and thickness of 25 ± 5 nm that uniformly covered the substrate with a high platelet density of 9 × 108 cm−2. The electrochemical performance of nano-platelets for lithium storage was studied in detail and compared with other morphologies of tin. Tin nano-platelets exhibited high reversible capacity and excellent cycling performance, the capacity was maintained at 820 mA h g−1 for 100 cycles and more, far superior to the other structures. Excellent rate capability was also observed for nano-platelets up to 5 C, with the ability to be operated at 20 C without damage. The superior electrochemical performance of tin platelets is mainly attributed to its two-dimensional structure that efficiently distributes strain, allowing high mechanical stability even after 100 cycles, as confirmed by Scanning Electron Microscopy (SEM).This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.Peer reviewe