Savojna svojstva lameliranog drva izrađenoga od topolovine i GFRP-a

In this study, 4 layers of 5 mm thick slats obtained by sawing method from poplar wood were used. Plain woven GRFP with low density and grammage of 100 g/m2 (Type 1) and plain woven GRFP with high density and grammage of 200 g/m2 (Type 2) were placed and glued between each layer. Polyvinyl acetate (PVAc-D4), Polyurethane (PU) and dual-component Epoxy (L285-resin and H285-hardener) adhesives were used for gluing the layers. Strength values (bending and modulus of elasticity) between the obtained layers were investigated. As a result of the study, it was determined that epoxy glue has higher strength than polyurethane and polyvinyl acetate glues; Type 2 plain woven fabric has higher strength than Type 1 plain woven fabric; and parallel load to the glue line results in higher performance than perpendicular load to the glue line.U radu se prikazuje istraživanje lameliranog drva izrađenoga od piljenjem proizvedenih topolovih platica debljine 5 mm složenih u četiri sloja. Između svakog sloja zalijepljena je plošno tkana GRFP tkanina male gustoće i površinske mase 100 g/m2 (tip 1) i plošno tkana GRFP tkanina velike gustoće i površinske mase 200 g/m2 (tip 2). Za lijepljenje drva i tkanine upotrijebljena su ova ljepila: polivinilacetatno (PVAc-D4), poliuretansko (PU) i dvokomponentno epoksidno (L285-mola i H285-otvrdnjivač). Istražene su vrijednosti čvrstoće (savijanje i modul elastičnosti) te je utvrđeno da epoksidno ljepilo ima veću čvrstoću nego poliuretansko i polivinilacetatno ljepilo. Nadalje, tkanina tipa 2 ima veću čvrstoću od tkanine tipa 1, a djelovanjem sile paralelno sa sljubnicom dobivena su bolja svojstva nego pri djelovanju sile okomito na sljubnicu