An Experimental Characterization of Ni2TiSi and Ni2CrSi Full-Heusler Alloys Related to Structural and Magnetic Properties

Ni2TiSi and Ni2CrSi triple and full Heusler alloys were synthesized in an arc melting furnace within thedesired stoichiometric ratio. Crystal structure was investigated by XRD analysis and the results show that thesamples are in Fm-3m (cubic) space group. Surface morphology was obtained by SEM-Mapping phaseimages with EDS analysis results and samples have both major and minor phases. The magneticcharacteristics of the materials were determined by using the M-T and M-H graphics. Linear behavior in theM-H curves clearly shows that the compounds are paramagnetic.This study was supported by Erciyes University BAP Research Foundation under the project numbers FDK2017-7359.