Repair bond strength of composite to Er,Cr:YSGG laser irradiated zirconia and porcelain surfaces

Background: Fracture or chipping are major concerning failures of an all-ceramic restoration. Repairing of the failure restoration using intra-oral technique is time saving and cost effective treatment modality. The present study was proposed to evaluate effect of Er,Cr:YSGG laser irradiation on shear bond strength between zirconia/porcelain and composite resin. Methods: Thirty zirconia and thirty zirconia based porcelain disc shape specimens were prepared. Three different surface treatment procedure were applied the specimens. For control groups (Group ZC and PC), instruction manual of an intra-oral porcelain repair system was followed. Different pulse rates of Er,Cr:YSGG laser irradiation (short and long pulses) were applied to zirconia and porcelain surfaces for other groups (Group ZS, ZL, PS, and PL). Porcelain repair kit was used to repair specimens using standard cylindrical teflon mold (2 x 2 mm). Repair bond strength of the repaired specimens was tested using a universal testing machine. Results: Highest mean bond strength value was observed at Group PC that was significantly higher than laser applied porcelain groups. Long pulse laser irradiation illustrated that increased mean bond strength compared to short pulse application on to the porcelain surface. Laser applied zirconia groups showed better mean bond strength than Group ZC, but differences between the groups were not statistically significant. Conclusion: Different modes of Er,Cr:YSGG laser irradiation enhanced repair bond strength of the composite resin to zirconia, but these were not significant. Following the instruction manual for surface treatment on the porcelain surface was better method than Er,Cr:YSGG laser surface conditioning