Change in the Positron Annihilation Lifetime of Vacancy Clusters Containing Hydrogen Atoms in Electron-Irradiated F82H

The change in the positron annihilation lifetime (PAL) of vacancy clusters before and after electrolysis hydrogen charging was determined using PAL measurements in electron-irradiated F82H. The experimental change indicated 8 hydrogen atoms were trapped in vacancy clusters; whereas the theoretical calculation resulted in approximately 14 atoms. As the samples were left at room temperature for 5 min until the start of the PAL measurements, the de-trapping effect of hydrogen atoms was also considered; approximately 13 hydrogen atoms were captured at each vacancy cluster. The PAL decreased after annealing at 148 K, which could not be explained theoretically. Therefore, further experiments and discussions are needed to obtain a precise change in the PAL of vacancy clusters containing hydrogen atoms in F82H