Development of crack sealant bending beam rheometer (CSBBR) testing to characterize hot-poured bituminous crack sealants at low temperatures

This paper presents a modified test for evaluating the rheological behavior of hot-poured bituminous crack sealants using a bending beam rheometer. The research was done to provide better correlation between sealant test characteristics and field performance than existing tests. The new test procedure includes new specimen geometry and preparation parameters, a specimen aging procedure, a validated testing period, and establishes a time at which stiffness is determined. Nine sealants with a wide range of rheological behaviors were tested between ?4\ub0C and ?40\ub0C. The new test procedure was used to ascertain the stiffness at 240s, the average creep rate, and the dissipated energy ratio of the test samples.Ce document pr\ue9sente un essai modifi\ue9 pour l'\ue9valuation du comportement rh\ue9ologique des scellants pour fissures bitumineux coul\ue9s \ue0 chaud, au moyen d'un rh\ue9om\ue8tre de flexion. On visait par cette recherche \ue0 obtenir une corr\ue9lation entre caract\ue9ristiques d'essai des scellants et performance in situ qui soit meilleure que celle des essais existants. La nouvelle m\ue9thode d'essai comprend de nouveaux param\ue8tres de g\ue9om\ue9trie et de pr\ue9paration des sp\ue9cimens, une proc\ue9dure de vieillissement des sp\ue9cimens, ainsi qu'une p\ue9riode d'essai valid\ue9e, et elle \ue9tablit un d\ue9lai pour la d\ue9termination de la rigidit\ue9. Neuf (9) scellants pr\ue9sentant une vaste gamme de comportements rh\ue9ologiques ont \ue9t\ue9 test\ue9s \ue0 des temp\ue9ratures allant de -4 \ub0C \ue0 -40 \ub0C. La nouvelle m\ue9thode a \ue9t\ue9 utilis\ue9e dans le but de d\ue9terminer la rigidit\ue9 \ue0 240 s, la vitesse de fluage moyenne et le rapport d'\ue9nergie dissip\ue9e des \ue9chantillons mis \ue0 l'essai.Peer reviewed: YesNRC publication: Ye