Properties of portland cement-silica fume pastes: I. Porosity and surface properties

Properties such as porosity, pore-size distribution, surface area and drying shrinkage are determined for silica fume- portland cement blends (0-30% silica fume) cured from 1 to 180 days at w/(c+sf) of 0.25 and 0.45. Porosity was measured by helium, mercury and water techniques. It is shown that in paste blends a discontinuous pore structure is formed after as little as seven days of curing due to reaction of Ca(OH)[2] with silica fume. The pores are not so large as those in mortars owing to the lack of interface effects. Total porosities of the blends can only be measured by a water technique, whereas for plain cement pastes other techniques are applicable.D\ue9termination de caract\ue9ristiques telles que la porosit\ue9, la r\ue9partition des pores par taille, leur superficie totale et le retrait au s\ue9chage pour des m\ue9langes ciment Portland-poussi\ue8re de silice (0-30%) apr\ue8s durcissement de 1 \ue0 180 jours avec des rapports e/(c+ps) de 0,25 et 0,45. La porosit\ue9 a \ue9t\ue9 mesur\ue9e au moyen de techniques utilisant l'h\ue9lium, le mercure et l'eau. On a constat\ue9 que dans les m\ue9langes de p\ue2te, une structure de pores discontinues se forme d\ue8s sept jours apr\ue8s le d\ue9but du durcissement par suite de la r\ue9action du Ca(OH)[2] avec la poussi\ue8re de silice. Les pores ne sont pas aussi gros que ceux des mortiers \ue0 cause de l'absence d'effets d'interface. Les porosit\ue9s totales des m\ue9langes ne peuvent \ueatre mesur\ue9es qu'au moyen de l'eau, tandis que pour les p\ue2tes de ciment ordinaires, il existe d'autres techniques.Peer reviewed: YesNRC publication: Ye