Interply adhesion and blistering of the bituminous built- up roofing membranes

Stresses in built-up roofing membranes are caused by differential movements due to loads, temperature variations, and moisture changes. If excessive over a period of time they cause premature failure of the membrane, the most common symptom being blistering and interply separation. The effect of moisture and applied pressure on the interply adhesion of built-up roofing membranes and on the development of blisters has been investigated. Some 200 specimens from different samples of built-up roofing membranes made with conventional Type 15 organic felt plies or with cotton fabric plies (denim cloth) were tested at varying amounts of moisture, surface pressure, and rate of loading. When the specimens were subjected to pull-off, peel, shear and blistering tests it was evident that adhesive bond is affected by: voids at the interface, moisture in the asphalt felt or fabric, perforations of the felt or fabric plies, compressive loads on the membrane surface and their duration prior to testing, viscoelastic behaviour of the binder.Les contraintes dans les membranes de couvertures multicouches sont caus\ue9es par des mouvements diff\ue9rentiels dus aux charges et aux variations de temp\ue9rature et d'humidit\ue9. Des contraintes trop \ue9lev\ue9es pendant une certaine p\ue9riode de temps, provoquent une d\ue9t\ue9rioration pr\ue9matur\ue9e de la membrane, qui se manifeste le plus souvent par des cloques et un manque d'adh\ue9rence entre les couches. On a \ue9tudi\ue9 les effets de l'humidit\ue9 et de la pression sur l'adh\ue9rence entre les couches des membranes de couvertures multicouches et sur la formation de cloques. Quelque 200 \ue9chantillons provenant de diff\ue9rentes membranes de couvertures bitumineuses multicouches faites d'\ue9paisseurs de feutre organique de type 15 ou de tissu de coton (denim) ont \ue9t\ue9 mis \ue0 l'essai dans diff\ue9rentes conditions d'humidit\ue9, de pression de surface et de charge. Les essais d'arrachement, de d\ue9collage, de cisaillement et de cloquage r\ue9alis\ue9s sur les \ue9chantillons ont d\ue9montr\ue9 que l'adh\ue9rence est fonction des facteurs suivants: vides \ue0 l'interface, humidit\ue9 dans le feutre asphalt\ue9 ou le tissu, perforations des \ue9paisseurs de feutre ou de tissu, charges de compression sur la surface de la membrane et dur\ue9e d'application de ces charges avant les essais, comportement visco\ue9lastique du liant.Peer reviewed: YesNRC publication: Ye