Comparison of mechanical properties of compacted calcium hydroxide and portland cement paste systems

Mechanical properties of Ca(OH)[2] are compared with those of portland cement paste at different porosities. Intrinsic values of modulus of elasticity (E) and microhardness (H) for Ca(OH)[2] compacts were obtained by extrapolating to zero porosity log E and log H versus porosity curves. The values for the Ca(OH)[2] and portland cement paste systems are of similar magnitude. Flexural strength values for both systems were also determined to be of similar magnitude for the porosity range studied. Fracture terms (K[c], J[c], G[ c], gamma [T]) were determined. K[c] and gamma [T] versus porosity plots for both systems revealed that these fracture terms are of similar magnitude in the porosity range common to both.Les caract\ue9ristiques m\ue9caniques de Ca(OH)2 sont compar\ue9es \ue0 celles de la p\ue2te de ciment Portland pour plusieurs porosit\ue9s. Les valeurs intrins\ue8ques du module d'\ue9lasticit\ue9 (E) et de la microduret\ue9 (H) des \ue9chantillons compacts de Ca(OH)2 ont \ue9t\ue9 obtenues par extrapolation \ue0 la porosit\ue9 nulle log E et log H en fonction des courbes de porosit\ue9. Les valeurs pour Ca(OH)2 et la p\ue2te de ciment Portland sont du m\ueame ordre. Les valeurs de la r\ue9sistance \ue0 la flexion des deux m\ue9langes se sont r\ue9v\ue9l\ue9es \ue9galement du m\ueame ordre de grandeur pour les porosit\ue9s envisag\ue9es au cours de l'\ue9tude. Les caract\ue9ristiques de rupture (Kc, Jc, Gc, gamma T) ont \ue9t\ue9 d\ue9termin\ue9es. Les graphes de Kc et gamma T en fonction de la porosit\ue9 pour les deux m\ue9langes ont montr\ue9 que les caract\ue9ristiques de rupture sont semblables pour les variations de porosit\ue9 envisag\ue9es communes aux deux m\ue9langes.Peer reviewed: YesNRC publication: Ye