Fracture toughness of autoclaved portland cement - silica mixtures

Fracture toughness measurements made at 11% RH on autoclaved cement/silica mixtures having a wide range of silica contents and porosities yielded a series of curves for K[c] versus porosity and K[c] versus silica content. Those for preparations having low porosity and silica content were unique. Apparently alphaC[2]S-hydrate, unreacted silica and pores having specific size distribution can act as crack arrestors. K[c] versus hardness curves were similar to those for K[c] versus porosity. Simple microhardness tests may be useful in predicting fracture toughness of autoclaved cementitious systems.Les mesures de la solidit\ue9 \ue0 la rupture de m\ue9langes ciment-silice autoclav\ue9s contenant 11% d'humidit\ue9 relative et des proportions diff\ue9rentes de silice et de vides ont permis de construire une s\ue9rie de courbes pour Kc en fonction de la porosit\ue9 et pour Kc en fonction de la teneur en silice. Les pr\ue9parations ayant une faible porosit\ue9 et une faible teneur en silice se comportaient de facon unique. Apparemment les hydrates C2S, la silice n'ayant pas r\ue9agi et les pores d'une certaine dimension peuvent agir comme r\ue9ducteurs de la fissuration. Les courbes Kc en fonction de la duret\ue9\ue9 taient similaires aux courbes Kc en fonction de la porosit\ue9. Des essais de microduret\ue9 simples peuvent \ueatre utilis\ue9s pour pr\ue9dire la solidit\ue9 \ue0 la rupture des m\ue9langes ciment\ue9s autoclav\ue9s.Peer reviewed: YesNRC publication: Ye