Hydration of cement : role of triethanolamine

Following addition of 0.1, 0.25, 0.35, 0.5 and 1.0 per cent triethanolamine, studies have been made of the hydration and hardening characteristics of (a) tricalcium aluminate, (b) tricalcium aluminate + gypsum, (c) tricalcium silicate, (d) dicalcium silicate, and (e) portland cement. Triethanolamine (TEA) accelerated the hydration of 3CaO.Al[2] O[3] and 3CaO.Al[2]O[3]-CaSO[4].2H[2]O systems and extended the induction period of the hydration of 3CaO.SiO[2]. In portland cement paste TEA decreased the strength of all ages and setting characteristics were drastically altered, especially at higher TEA contents. Evidence was obtained also of the formation of a complex of TEA with the hydrating silicate phase.On a \ue9tudi\ue9 l'hydratation et les caract\ue9ristiques de durcissement a) de l'aluminate tricalcique, b) de l' aluminate tricalcique + gypse, c) du silicate tricalcique, d) du silicate bicalcique, et e) du ciment portland, apr\ue8s l' addition de 0.1, 0.25, 0.35, 0.5, et 1.0 pour cent de tri\ue9 thanolamine (TEA). La TEA acc\ue9l\ue8re l'hydratation des syst\ue8 mes de 3CaO.Al[2]O[3] et de 3CaO.Al[2]O[3]-CaSO[4].2H[2]O et prolonge la p\ue9riode d'induction de l'hydratation de 3CaO.SiO[ 2]. Pour ce qui est de la p\ue2te de ciment portland, la TEA r\ue9 duit sa r\ue9sistance pour tous les degr\ue9s de vieillissement et modifie profond\ue9ment ses caract\ue9ristiques de durcissement, surtout pour les teneurs plus \ue9lev\ue9es en TEA. On obtient \ue9 galement des indications de la formation d'un complexe de TEA avec la phase de silicate en hydratation.Peer reviewed: YesNRC publication: Ye