Mobility of Edge Dislocations in the Basal‐Slip System of Zinc

This paper presents the results of measurements of the velocities of 〈1210〉 (0001) edge dislocations in zinc as a function of applied shear stress. All tests were conducted at room temperature on 99.999% pure zinc monocrystals. Dislocations were revealed by means of the Berg‐Barrett x‐ray technique. Stress pulses of microsecond duration were applied to the test specimens by means of a torsion testing machine. Applied resolved shear stresses ranged from 0 to 17.2×10^6 dyn∕cm^2 and measured dislocation velocities ranged from 40–700 cm∕sec. The results of this study indicate that the velocity of edge dislocations in the basal slip system of zinc is linearly proportional to the applied resolved shear stress. These results are analyzed in terms of the phonon drag theory. Agreement between this theory and the results reported here is quite good