Factors affecting the performance of metakaolin geopolymers exposed to elevated temperatures

The effects of geopolymer binder systems exposed to elevated temperatures are examined. Geopolymers investigated were synthesized from metakaolin, activated by combinations of sodium/potassium silicate and sodium/potassium hydroxide. The specimens were then exposed to temperatures of 800 °C. The factors studied were: (1) calcining temperatures of kaolin; (2) Si/Al ratio of the geopolymer; (3) activator/metakaolin ratio; (4) curing temperature; and (5) alkali cation type. Altogether 30 geopolymer formulations were studied. The samples were subjected to compressive strength, thermogravimetry, and scanning electron microscopy tests. Results showed that Si/Al ratio has a significant influence on elevated temperature exposure deterioration. Lesser strength loss due to elevated temperature exposures were observed in geopolymer with high Si/Al ratios (>1.5). The geopolymer binders activated by potassium-based activators showed an enhanced post-elevated temperature exposure performance compared to sodium-based systems. The optimum calcining temperature of kaolin and curing temperatures for improved temperature performance are also reported