Birch dynamic and static modulus of elasticity comparison on different moisture levels

Antud bakalaureusetöö annab ülevaate kasepuidu staatilise ja dünaamilise elastusmooduli võrdlemisest erinevatel niiskustasemetel. Samuti uuriti ultraheli levimise kiiruse ja niiskussisalduse vahelisi seoseid. Lisaks üritati puidu dünaamilise elastsusmooduli ja tiheduse kaudu prognoosida puidu purunemismoodulit. Töös kasutati 30 katsekeha, mis kuivatati 6-le erinevale niiskustasemele. Niiskuste muutumine toimus vahemikus 86,6-0%. Iga niiskustaseme juures tehti viie katsekehaga ultraheli- ja lineaarmõõtmete mõõtmised. Lõpuks mõõdeti puidukatsemasinal Instron puidu elastsus- ja purunemismoodulit. Üldised võrdlused staatilise ja dünaamilise elastsusmooduli vahel tehti niiskustasemel alla ja üle 30%. Selgus, et ultraheli levimise kiiruse ja niiskussisalduse vaheline seos on suurim üle 30% niiskustasemel pikisuunas, R= -0,47. Alla 30% niiskussisalduse on ultraheli levimise kiiruse ja niiskussisalduse vaheline seos suurim tangentsiaalses suunas, R= 0,53. Purunemismooduli prognoos dünaamilise elastsusmooduli kaudu osutus üle 30% niiskussisalduse juures usaldusväärseks kõigis suundades: tangentsiaal-,radiaal- ja pikisuund. Alla 30% niiskussisalduse juures oli purunemismooduli prognoos dünaamilise elastsusmooduli kaudu usaldusväärne tangentsiaal- ja radiaalsuunal. Samuti näitasid katsed, et paindetugevuse prognoos tiheduse järgi osutub mõistlikuks üle 30% niiskussisaldusega puidu korralThis bachelor thesis gives an overview of the comparison of birch alder wood static and dynamic modulus of elasticity in different moisture levels. Also investigated the relationships between the ultrasonic velocity and moisture content. In addition tried to predict the modulus of rupture by density and modulus of dynamic. For the study I used 30 test-pieces, which was dried for six different levels of humidity. Changes in moisture was in the range of 86.6 to 0%. In every six different levels of humidity were made linear and ultrasound measurements by 5 test-pieces. At the end were measured the modulus of elasticity and modulus of rupture by wood testing machine Instron. General comparisons between static and dynamic modulus of elasticity were made with moisture level lower and higher than 30%. Test showed that relationship between ultrasonic velocity and moisture content over 30% of moisture content is the largest for the longitudinal direction, R= -0,47. Lower than 30% of moisture content is the relationship between ultrasonic speed and moisture content largest for the tangential direction, R=0,53. The modulus of rupture prognosis by dynamic modulus of elasticity proves to be a reliable over 30% of moisture content in every direction: tangential-, radial- and longitudinal direction. Less than 30% of moisture content was modulus of rupture prognosis by dynamic modulus of elasticity reliable in tangential and radial direction. The tests also showed that it is reasonable to predict the bending strength by density only over 30% of moisture conten