PREPARASI FOTOKATALIS KARBON AKTIF/?-FE2O3 MENGGUNAKAN METODE HIDROTERMAL SERTA APLIKASINYA PADA DEGRADASI ZAT WARNA TARTRAZIN

ABSTRAKModifikasi hematit (?-Fe2O3) dengan karbon aktif untuk mendapatkan kompositKarbon Aktif/?-Fe2O3 melalui metode hidrotermal dan uji aktivitas fotokatalitiknyapada degradasi zat warna tartrazin telah dilakukan. Hematit yang digunakan berasaldari pasir besi yang diperoleh dari pantai Syiah Kuala, Deah Raya, Aceh Besar yangdiekstraksi menggunakan asam klorida (HCl) dan dikopresipitasi menggunakanammonium hidroksida (NH4OH). Karbon aktif yang digunakan berasal dari patiumbi janeng yang dikarbonisasi melalui metode hidrotermal dan diaktivasimenggunakan asam klorida (HCl). Karakterisasi produk dilakukan menggunakaninstrumen X-Ray Diffraction (XRD), Scanning Electron Microscopy-EnergyDispersive X-Ray Spectroscopy (SEM-EDS) dan Brunaeur Emmet Teller (BET).Hematit yang disintesis menunjukkan bahwa hematit telah terbentuk dengan fasa ?-Fe2O3, karbon aktif memiliki fasa amorf dan komposit KA/?-Fe2O3 memiliki ukuranrata-rata partikel sebesar 26,54 nm. Hasil uji aktivitas menunjukkan bahwa kompositKA/?-Fe2O3 dapat mendegradasi zat warna tartrazin hingga 69,49% di bawah sinarUV dan 95,39% di bawah sinar matahari. Aktivitas fotokatalitik tersebut diperolehpada kondisi optimum pH 1, massa fotokatalis 350 mg dan konsentrasi awal zatwarna tartrazin 12,5 ppm dengan waktu radiasi selama 210 menit di bawah sinar UVsedangkan radiasi sinar matahari membutuhkan waktu selama 180 menit.Kata kunci : Hematit, karbon aktif, pati umbi janeng, komposit Karbon Aktif/?-Fe2O3, tartrazin dan fotokatalis.ABSTRACTModification of hematite (?-Fe2O3) with activated carbon to produce ActivatedCarbon/?-Fe2O3 composite by hydrothermal method and its photocatalytic activityon the degradation of tartrazine dye was conducted carried out. Hematite wasobtained from iron sand taken from Syiah Kuala beach, Deah Raya, Aceh Besarwhich was extracted by using hydrochloric acid (HCl) and coprecipitated usingammonium hydroxide (NH4OH). Activated carbon was derived from janeng tuberstarch which was carbonized by hydrothermal method and activated usinghydrochloric acid (HCl). The material were characterized by using X-Ray Difraction(XRD), Scanning Electron Microscopy-Energy-Dispersive X-Ray Spectroscopy(SEM-EDS) and Brunaeur Emmet Teller (BET). Iron (III) oxide extracted from ironsand is ?-Fe2O3 phase and activated carbon has an amorphous phase. AC/?-Fe2O3composite has an average crystallite size of 26,54 nm. The result of photocatalyticactivity showed that C/?-Fe2O3 composite can remove tartrazine up to 69,49% underUV light and 95,39% under sunlight. This highest photocatalytic activity wasobtained on optimum conditions at pH 1, a photocatalyst mass of 350 mg and initialtartrazine of 12,5 ppm under UV light irradiation for 210 min and under sunlightirradiation for 180 min.Keywords: Hematite, activated carbon, janeng tuber starch, Activated Carbon/?-Fe2O3 composite, tartrazine and photocatalyst