Influence of semi-solid casting and equal channel pressing on microstructure of a hypoeutectic Al-Si alloy

The aim of this work was to develop understanding of microstructural evolution of the alloy casted in semi-solid condition using a cooling slope and conventional casting followed by ECAP in a 120 die. Feed materials were prepared by cooling slope casting and conventional casting for ECAP process. The microstructures and Vickers hardness of the worked materials extruded by two routes (A and B) were evaluated. The primary α-Al phase tends to be elongated after processing by route A. However, its morphology was similar in nature to the microstructure of the as-cast sample after processing by route B. The Si particles become fragmented during ECAP processing and are more nearly globular in shape and uniform in size than in the as-cast sample. The microstructure of the semi-solid cast ECAPed samples was more homogenous than that of the conventional cast ECAPed sample followed by ECAP for both routes. The hardness of semi-solid cast ECAP samples was also higher than that of conventional cast ECAPed samples for both routes