Desarrollo y control de microestructuras en superconductores REBa2Cu3O7 (RE=Y,Nd) solidificados direccionalmente

[EN] Directionally solidified ReBa2Cu3O7 (RE=Nd,Y) superconductors display a complex microstructure which is generated during the solidification and annealing processes. The various defects influence the superconducting properties in different ways. The present article briefly reviews the characteristics of the different defect structures and evolution in connection with their effect on the critical currents. In this work, defects are classified into strong pinning centres and currents limiting defects. Dislocation problems are addressed separately, emphasising on the generation of stacking faults, oxygenation effects and plastic deformation processing.[ES] Los superconductores de composición REBa2Cu3O7 (RE=Y,Nd) preparados mediante solidificación direccional presentan una microestructura compleja que se desarrolla durante las etapas de solidificación y tratamientos de recocido posteriores. Los diversos defectos influyen sobre las propiedades superconductoras de manera desigual. El presente artículo revisa brevemente las características de las diferentes estructuras de defectos y su evolución conectando con su efecto sobre las corrientes críticas. Los defectos, en este trabajo, se clasifican en centros fuertes de anclaje de flujo y defectos que limitan la corriente. Los problemas asociados con las dislocaciones se tratan separadamente, poniendo el énfasis en la generación de defectos de apilamiento, problemas de oxigenación y deformación plástica.Peer reviewe