Flexural and Morphological Properties of Epoxy/Glass Fibre/Silane- Treated Organo-montmorillonite Composites

Abstract: Organo-montmorillonite (OMMT) was treated with 3-aminopropyltrimethoxysilane. Epoxy (E) composites reinforced with glass fibber (GF) and /GF/OMMT composites was investigated using scanning electron microscopy (SEM). It is interesting to note that parts of the silane-treated OMMT also adhered to the GF, which can promote better interfacial interaction and wettability between the E and GF. Keywords: silane coupling agent, exfoliated epoxy nanocomposites, organomontmorillonite Abstrak: Organo-montmorillonit (OMMT) telah dirawat dengan 3-aminopropiltrimetoksisilana. Komposit epoksi (E) diperkuatkan gentian kaca (GF) dan OMMT telah disediakan dengan menggunakan teknik 'hand-lay up'. Sifat-sifat pelenturan bagi komposit E/GF/OMMT telah dicirikan dengan ujian pelenturan tiga titik. Modulus dan kekuatan pelenturan bagi komposit E/GF telah dipertingkat dengan penambahan OMMT-dirawatkan silana. Kebolehan eksfoliasi bagi OMMT dalam E telah dikaji dengan menggunakan pembelauan sinar-X (XRD). Adalah didapati bahawa lapisan silikat OMMT telah berjaya dieksfoliasikan dalam E. Morfologi permukaan peretakan akibat pelenturan bagi komposit E/GF/OMMT telah diselidik dengan menggunakan mikroskopi elektron penskanan (SEM). Yang menarik, didapati bahawa sebahagian OMMT-dirawatkan silana melekat di permukaan GF, yang boleh memberikan interaksi antara fasa dan keboleh-pembasahan yang lebih baik antara E dengan GF. Kata kunci: agen pengkupelan silana, nanokomposit epoksi tereksfoliasi, organomontmorilloni