Uji Kulit Nanas, Umbi Gadung Dan Limbah Cair Pulp Kakao Sebagai Koagulan Lateks Terhadap Mutu Karet

Beberapa petani karet di Indonesia menggunakan koagulan lateks non anjuran sehingga merusak mutu kualitas bokar. Pemanfaatan koagulan lateks organik diprediksi berpotensi untuk memperbaiki mutu karet. Oleh karena itu, penelitian ini bertujuan untuk mengetahui  pengaruh dari ekstrak kulit nanas, ekstrak umbi gadung dan limbah cair hasil fermentasi pulp kakao sebagai koagulan lateks terhadap mutu karet. Penelitian menggunakan Rancangan Acak Kelompok Lengkap dengan enam perlakuan, yaitu 10 ml; 20 ml ekstrak kulit nanas, 10 ml; 20 ml ekstrak umbi gadung dan 10 ml; 20 ml limbah cair hasil fermentasi pulp kakao. Parameter yang diamati adalah waktu kontak, bobot karet, karakteristik koagulum, yang terdiri dari kejernihan serum, warna koagulum dan bau busuk koagulum, kadar abu dan kadar zat menguap sesuai Standart Indonesian Rubber (SIR) 20. Hasil penelitian menunjukkan 20 ml koagulan lateks mampu menghasilkan waktu kontak yang lebih cepat dan meningkatkan bobot karet. Selain itu, juga menghasilkan mutu bokar dengn sedikit berbau busuk yang lebih baik dari hasil bokar oleh koagulan anorganik.Some rubber farmers in Indonesia use un-recommended latex coagulant and it causes bad quality of rubber. The utilization of organic latex coagulants has the potential way to improve rubber quality. The aim of this study was to determine the effect of pineapple exocarp extract, gadung tuber extract and liquid of pulp cocoa fermentation as latex coagulants toward rubber quality. The study was using Randomized Completely Block Design with six treatments and four replications the treatments tested was 10 ml and 20 ml pineapple exocarp extract, 10 ml and 20 ml gadung extract and 10 ml and 20 ml liquid of pulp cocoa fermentation. The parameters observed were contact time, weight of rubber and rubber characteristic which are comprised of serum clarity, rubber color and rubber stinky smell produced, ash content and volatile matter compared to Standart Indonesian Rubber (SIR) 20. The result of this study showed that 20 ml latex coagulant had faster contact time than others and increased weight of the rubber. It showed that rubbers produced a bit stinky smell as well, it was better than rubbers produced by inorganic latex coagulant