Thermal stability of lanthanum zirconate plasma-sprayed coating

Lanthanum zirconate (La2Zr2O7, LZ) is a newly proposed material for thermal barrier coatings (TBCs). The thermal stability of LZ coating was studied in this work by long-term annealing and thermal cycling. After long-term annealing at 1400 degreesC or thermal cycling, both LZ powder and plasma-sprayed coating still kept the pyrochlore structure, and a preferred crystal growth direction in the coating was observed by X-ray diffraction. A considerable amount of La2O3 in the powder was evaporated in the plasma flame, resulting in a nonstoichiometric coating. Additionally, compared with the standard TBC material yttria-stabilized zirconia (YSZ), LZ coating has a lower thermal expansion coefficient, which leads to higher stress levels in a TBC system