Crystal structure of apatite type Ca2.49Nd7.51(SiO4)6O1.75

The title compound, Ca2+xNd8–x(SiO4)6O2–0.5x (x = 0.49), was synthesized at 1873 K and rapidly quenched to room temperature. Its structure has been determined using single-crystal X-ray diffraction and compared with results reported using neutron and X-ray powder diffraction from samples prepared by slow cooling. The single-crystal structure from room temperature data was found to belong to the space group P63/m and has the composition Ca2.49Nd7.51(SiO4)6O1.75 [dicalcium octaneodymium hexakis(orthosilicate) dioxide], being isotypic with natural apatite and the previously reported Ca2Nd8(SiO4)6O2 and Ca2.2Nd7.8(SiO4)6O1.9. The solubility limit of calcium in the equilibrium state at 1873 K was found to occur at a composition of Ca2+xNd8–x(SiO4)6O2–0.5x, where x = 0.49.status: publishe