Add to ORKGThe cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic inspection, chemical composition analysis, microstructure analysis, hardness test, mechanical properties test and dimension inspection. The analysis results show that: All of its chemical composition, microstructure, hardness, mechanical properties and dimensions accord with the technical specifications. However, due to the bearing score of the seventh main journal and the wear of fillet, the crankshaft cracked at multi-points from the fillet. The reason is that the fracture of crankshaft is finally caused by large cyclic external force
Akhmad Khumaidi Bisri, 2018 NIT: 50134958. T, “Analysis of 3rd Diesel Generator Crankshaft’s Cracks...
AbstractDuring the inspection of a North Sea oil and gas platform a crack was identified on the cran...
The main objective of writing this report on the failure of crankshaft is to investigate the charact...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
In this paper, the macroscopic observation and chemical composition analysis of the third crankshaft...
The crankshaft of diesel engine of a heavy duty vehicle broke during running. By means of macroscopi...
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
In this study, failure analysis of a crankshaft was carried out. The crankshaft made of nodular grap...
Based on the analysis of the fracture of a certain type of QT800-2 nodular cast iron crankshaft, the...
Study on the fracture specimen of EB03 crankshaft which produced by a crankshaft company. It is foun...
This paper presents the failure analysis of a diesel engine crankshaft used in a truck. An evaluatio...
This paper reports a failure mode analysis of a 1900 cm(3) turbo diesel engine of a well-known comme...
Szczególnym rodzajem zużycia elementów pojazdów są różnego rodzaju uszkodzenia, w tym pęknięcia. W a...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
AbstractA failure analysis of two damaged crankshafts are presented: one obtained from a diesel engi...
Akhmad Khumaidi Bisri, 2018 NIT: 50134958. T, “Analysis of 3rd Diesel Generator Crankshaft’s Cracks...
AbstractDuring the inspection of a North Sea oil and gas platform a crack was identified on the cran...
The main objective of writing this report on the failure of crankshaft is to investigate the charact...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
In this paper, the macroscopic observation and chemical composition analysis of the third crankshaft...
The crankshaft of diesel engine of a heavy duty vehicle broke during running. By means of macroscopi...
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
In this study, failure analysis of a crankshaft was carried out. The crankshaft made of nodular grap...
Based on the analysis of the fracture of a certain type of QT800-2 nodular cast iron crankshaft, the...
Study on the fracture specimen of EB03 crankshaft which produced by a crankshaft company. It is foun...
This paper presents the failure analysis of a diesel engine crankshaft used in a truck. An evaluatio...
This paper reports a failure mode analysis of a 1900 cm(3) turbo diesel engine of a well-known comme...
Szczególnym rodzajem zużycia elementów pojazdów są różnego rodzaju uszkodzenia, w tym pęknięcia. W a...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
AbstractA failure analysis of two damaged crankshafts are presented: one obtained from a diesel engi...
Akhmad Khumaidi Bisri, 2018 NIT: 50134958. T, “Analysis of 3rd Diesel Generator Crankshaft’s Cracks...
AbstractDuring the inspection of a North Sea oil and gas platform a crack was identified on the cran...
The main objective of writing this report on the failure of crankshaft is to investigate the charact...