Impaction bone grafting with freeze-dried irradiated bone. Part II. Changes in stiffness and compactness of morselized grafts: experiments in cadavers.

In the technique of impaction bone grafting, implant stability depends on the mechanical properties of the impacted morselized grafts. Although the procedure is usually performed with fresh-frozen femoral heads, there is still some concern about their supply and safety. Bone processing is a potential solution, but the mechanical properties of this material during and after impaction need to be determined. We used 6 osteoarthrotic femoral heads to prepare two paired batches of morselized bone. One batch was morselized and frozen. The other batch was chemically treated, morselized, freeze-dried and then gamma-irradiated. We impacted 18 samples from each batch in a contained cylinder. Freeze-dried bone grafts were tested after 30 minutes of rehydration. The changes in the compactness and stiffness of the material were monitored during the impaction. The compaction of the freeze-dried bone was faster than that of their fresh-frozen control. The maximal stiffness reached by both materials was the same (55 MPa), but the freeze-dried grafts required three to four times fewer impactions to achieve that stiffness. After 3, 10 and 50 impactions the freeze-dried bone was stiffer than the fresh-frozen bone. As it is easier to impact, the freeze-dried bone may be mechanically more efficient than the fresh-frozen bone in surgical conditions. Moreover, the processed bone meets the highest safety standards, as regards the risk of disease transmission