On-chip stress relaxation testing method for freestanding thin film materials

A stress relaxation method for freestanding thin films is developed based on an on-chip internal stress actuated microtensile testing set-up. The on-chip test structures are produced using microfabrication techniques involving cleaning, deposition, lithography, and release. After release from the substrate, the test specimens are subjected to uniaxial tension. The applied load decays with the deformation taking place during relaxation. This technique is adapted to strain rates lower than 10-6/s and permits the determination of the strain rate sensitivity of very thin films. The main advantage of the technique is that the relaxation tests are simultaneously performed on thousands of specimens, pre-deformed up to different strain levels, for very long periods of time without monopolizing any external mechanical loading equipment. Proof of concept results are provided for 205-nm-thick sputtered AlSi0.01 films and for 350-nm-thick evaporated Pd films showing unexpectedly high relaxation at room temperature