Odporność na korozję chlorkową podwodnego betonu naprawczego dojrzewającego w warunkach oddziaływania ciśnienia hydrostatycznego

The paper presents the results of the study of underwater repair concrete under the effect of the salt mist. The research was conducted in accordance with the standard PN-EN 14147. Concrete samples for testing the corrosive elements of that test were taken during the first 7 days of insight in the pressure vessel and were subjected to hydrostatic pressure effects from 0,1 to 0,5 MPa. The beneficial effect of hydrostatic pressure on the corrosion resistance of tested concrete repair was. Was observed samples taken from the surface layers of the tested elements showed slightly higher resistance to chlorides which confirmed the characteristics of pore distribution of concrete in the studies.W pracy przedstawiono wyniki badań podwodnego betonu naprawczego dojrzewającego w warunkach zmiennego ciśnienia hydrostatycznego, poddanego oddziaływaniu mgły solnej. Badania przeprowadzono zgodnie z normą  PN-EN 14147. Próbki betonu do badań korozyjnych pobrano z elementów próbnych, które przez okres pierwszych 7 dni dojrzewały w zbiorniku ciśnieniowym i poddane były oddziaływaniu ciśnienia hydrostatycznego o wartościach od 0,1 do 0,5 MPa. Stwierdzono korzystny wpływ ciśnienia hydrostatycznego na odporność korozyjną badanego betonu. Próbki pobrane z warstw przypowierzchniowych badanych elementów wykazały nieznacznie większą odporność na działanie chlorków co znalazło potwierdzenie w badaniach charakterystyki rozkładu porów badanych betonów