Synthesis of Hierarchical Zeolites with Morphology Control: Plain and Hollow Spherical Beads of Silicalite-1 Nanosheets

Binderless pure silica zeolites (zeosils) spheres and hollow spheres with a diameter of 20 µm composed of silicalite-1 nanosheets particles were prepared by pseudomorphic transformation of spherical silica beads using different temperatures (110, 130, and 150 °C) and treatment times (1–5 days) in order to adapt the local dissolution rate of silica to the crystallization rate of silicalite-1 nanosheets allowing to preserve the initial morphology of the silica beads. Fully crystalline beads of 20 µm were obtained at 110 °C for 5 days, whereas hollow spheres similar in size were synthesized at higher temperatures. The crystallization process seems to begin at the outer surface of the amorphous silica beads and spreads with the time in the interior of the beads leading to a dissolution of the inner amorphous part of the beads to create zeosil hollow spheres for the highest treatment temperatures (130 and 150 °C). The dissolution rate of the inner amorphous part of the beads increases by increasing the hydrothermal treatment temperature from 130 to 150 °C. The silicalite-1 beads synthesized at 110 °C for 5 days showed to be promising for rapid molecular decontamination by adsorbing n-hexane in larger amount than the silicalite-1 conventional big crystals in powder forms.Special Issue Microporous/Mesoporous Inorganic Material