Add to ORKGThe test material of a high temperature furnace is coke. in order to study the influence of temperature on the reactivity of coke, the reactivity index and weight loss rate of coke were measured under different reaction temperature conditions, and the dynamic observation of coke reaction process was made under the microscope. The reaction mechanism of coke was analyzed, and the influence of temperature on metallurgical properties was evaluated
In the paper behavior of the blast-furnace coke in the high temperature was presented. Comparative a...
Coke quality in blast furnace is measured by its resistance to degradation, in its role as a fuel, a...
Steel industries around the world have been trying to improve the blast furnace efficiency in order ...
The test material of a high temperature furnace is coke. in order to study the influence of temperat...
The reactivity index of weight loss (RI) and tumbling strength after the reaction (I10600) of manufa...
Abstract The blast furnace – basic oxygen furnace route remains the most utilised process route in ...
In this study the suitability of a laboratory analogue for coke for studying the reactivity of coke ...
In blast furnace ironmaking, efforts are made to decrease the coke consumption mainly by increasing ...
Physical and chemical properties of coke samples excavated from LKAB's Experimental Blast Furnace (E...
The reaction characteristics and mechanism of coke with different coke reactivity indices (CRIs) in ...
© 2015 Institute of Materials, Minerals and Mining. The aim of the present work is to adapt tests th...
Raising pulverized coal injection (PCI) will decrease coke rate, but increase the residence time ...
The present work aims to study the high-temperature strength of coke. Mechanisms of disintegration w...
In order to evaluate coke strength in a blast furnace, coke was subjected to (1) in-situ heating con...
The efficiency in use of reducing agents in blast furnace (BF) ironmaking has been significantly imp...
In the paper behavior of the blast-furnace coke in the high temperature was presented. Comparative a...
Coke quality in blast furnace is measured by its resistance to degradation, in its role as a fuel, a...
Steel industries around the world have been trying to improve the blast furnace efficiency in order ...
The test material of a high temperature furnace is coke. in order to study the influence of temperat...
The reactivity index of weight loss (RI) and tumbling strength after the reaction (I10600) of manufa...
Abstract The blast furnace – basic oxygen furnace route remains the most utilised process route in ...
In this study the suitability of a laboratory analogue for coke for studying the reactivity of coke ...
In blast furnace ironmaking, efforts are made to decrease the coke consumption mainly by increasing ...
Physical and chemical properties of coke samples excavated from LKAB's Experimental Blast Furnace (E...
The reaction characteristics and mechanism of coke with different coke reactivity indices (CRIs) in ...
© 2015 Institute of Materials, Minerals and Mining. The aim of the present work is to adapt tests th...
Raising pulverized coal injection (PCI) will decrease coke rate, but increase the residence time ...
The present work aims to study the high-temperature strength of coke. Mechanisms of disintegration w...
In order to evaluate coke strength in a blast furnace, coke was subjected to (1) in-situ heating con...
The efficiency in use of reducing agents in blast furnace (BF) ironmaking has been significantly imp...
In the paper behavior of the blast-furnace coke in the high temperature was presented. Comparative a...
Coke quality in blast furnace is measured by its resistance to degradation, in its role as a fuel, a...
Steel industries around the world have been trying to improve the blast furnace efficiency in order ...