A Comparative study of two copper(II) based metal-organic frameworks : Cu2¼(OH)½B4C•8H2O and Cu2Na(OH)B4C•7H2O

This study focussed on two copper(II)-containing metal-organic frameworks (MOFs): Cu2Na(OH)B4C•7H2O and Cu2¼(OH)½B4C•8H2O (B4C = 1,2,4,5- benzenetetracarboxylate). They are both covalent, three-dimensional metalorganic framework polymers containing voids filled with water molecules. Both were characterised by elemental analysis, infrared spectroscopy, X-ray powder diffractometry (both in situ and regular), thermogravimetric analysis, differential scanning calorimetry and X-ray photoelectron spectroscopy. These two MOFs are essentially identical, with the only difference being the substitution of sodium by copper at every 4th site (disordered throughout the crystal). The guest inclusion properties of both MOFs were studied and compared. Although both structures collapse on dehydration, it was observed that Cu2Na(OH)B4C•7H2O is able to take up signifcant amounts of water, methanol and ethanol. All these processes are fully reversible. Car-Parrinello molecular dynamics studies suggest that it is a strong interaction between the oxygen atoms on these molecules with the sodium cation of the MOF that is responsible for this signifcant uptake. In contrast, Cu2¼ (OH)½ B4C•8H2O, the MOF without a sodium cation, did not demonstrate any methanol or ethanol uptake, but was able to take up some water. The uptake of water, however, is not a fully reversible process. The absence of sodium likely results in insuffcient energy to draw methanol and ethanol into the framework, while a subtle rotation of a carboxylate group on dehydration decreases the ability of the framework to form hydrogen bonds, thus reducing the ability to take up water. A series of hydrothermal syntheses were performed in order to develop a method of synthesis superior to the current gel-based synthesis that requires several months and has poor yields. The hydrothermal products were characterized by elemental analysis, infrared spectroscopy, X-ray powder diffractometry, thermogravimetric analysis and differential scanning calorimetry. It was shown that the MOF Cu2Na(OH)B4C•7H2O may be synthesised in almost 100% yield by using a temperature of 120°C over a period of 72 hours. It was not possible to synthesise Cu2¼ (OH)½ B4C•8H2O in a 100% yield - it was only obtained as a minor product