p-n junction organic photovoltaics fabricated by all solution processing

We have prepared p-n junction organic photovoltaic cells using an all solution processing method with poly(3-hexylthiophene) (P3HT) as the donor and phenyl-C 61-butyric acid methyl ester (PCBM) as the acceptor. Interdigitated donor/acceptor interface morphology was observed in the device processed with the lowest boiling point solvent for PCBM used in this study. The influences of different solvents on donor/acceptor morphology and respective device performance were investigated simultaneously. The best device obtained had characteristically rough interface morphology with a peak to valley value ∼15 nm. The device displayed a power conversion efficiency of 1.78%, an open circuit voltage (V oc) 0.44 V, a short circuit current density (J sc) 9.4 mA/cm 2 and a fill factor 43%