Ultrafini prah cink-metatitanata veličine čestica 40 do 80 nm podvrgnut je prilikom sintetskog dela tretmana uticajima pritiska i temperature korišćenjem procesa presovanja i reakcionog sinterovanja. S obzirom na nestabilnost praha posmatran je odgovor sistema na ova dva tretmana. Usled navedenih uticaja došlo je do specifičnih promena svojstava ispresaka i sinterovanih uzoraka. Što se presovanja tiče urađen je set ispresaka kompaktiranih na različitim pritiscima uniaksijalnim dvostranim načinom presovanja. Metode karakterizacije ispresaka koje su korišćene su: merenje gustine ispresaka, merenje specifične površine metodom adsorpcije azota na niskim temperaturama, određivanje poroznosti metodom živine porozimetrije. Za opisivanje fenomena p...
ZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were characterised by means of T...
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during ...
In this study we have combined two research methods: structure prediction of ZnTiO3 using computatio...
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were treated...
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were trea...
Metastabile nanopowder ZnTiO3 pressed into cylindrical compacts at 200 MPa was submitted to conventi...
PhD defence presentation. The thesis "Sintering and Properties of Sintered ZnTiO3" was defended at t...
Sintering is often accompanied with phase transition. Phase transition kinetic is thushard to deconv...
International audienceZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were chara...
ZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were characterised by means of T...
Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Si...
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during ...
ZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were characterised by means of T...
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during ...
In this study we have combined two research methods: structure prediction of ZnTiO3 using computatio...
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were treated...
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were trea...
Metastabile nanopowder ZnTiO3 pressed into cylindrical compacts at 200 MPa was submitted to conventi...
PhD defence presentation. The thesis "Sintering and Properties of Sintered ZnTiO3" was defended at t...
Sintering is often accompanied with phase transition. Phase transition kinetic is thushard to deconv...
International audienceZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were chara...
ZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were characterised by means of T...
Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Si...
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during ...
ZnTiO3 nanopowders were obtained by sol-gel method. The nanopowders were characterised by means of T...
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during ...
In this study we have combined two research methods: structure prediction of ZnTiO3 using computatio...