Svojstva spoja u dvokovinskim motkama Cu-Al i Cu-čeliku nakon platiranja eksplozivom i valjanja

In the paper the microhardness, the microstructure and the bond strength of interface of bimetallic joint on the cross sections of the test bar have been investigated. For the experimental analysis, a bimetallic bar was manufactured using an explosive technique method and the process of rolling. For tests, 23 sets of specimens were prepared each consisting of copper tubes (grade M1-E), rolled steel rods (grade St3S), drawn rods (grade 55) and aluminium rods (grade PA6). The copper tubes and the steel and aluminium rods had different diameters, owing to which different distances between the rods and the internal tube walls were obtained. The results of the research show a significant deviation in microhardness distribution in the both layers near the joining border.U radu su prikazani rezultati istraživanja mikrotvordoće, mikrostrukture i čvrstoće sljubljivanja dvokovinskog spoja na presijeku ispitne šipke. Za potrebe eksperimentalne analize dvokovinska šipka je izrađena metodom primjene eksploziva i naknadnog valjanja. Za ispitivanja su pripremljena 23 kompleta uzoraka od kojih se svaki sastoji iz kompleta cijevi (kvaliteta M1-E), valjanih čeličnih šipki (kvalitete St35), vučenih šipki (kvaliteta 55) i aluminijskih šipki (kvaliteta PA6). Bakarne cijevi i čelične i aluminijske šipke su imale su imale različite promjere zbog kojih su dobivene različite udaljenosti između šipki i unutrašnjih stijenki cijevi. Rezultat ispitivanja pokazuje u oba sloja značajnu odstupanja u raspodjeli mikrotvrdoće uz granicu spoja